| Dimension Details | |||
|---|---|---|---|
| Inches | mm | Size (L * W) | ㎡ / Roll |
| 3/4" | 20 | 10 × 1 | 10 |
| 1" | 25 | 8 × 1 | 8 |
Main Material Composition:
ULT: Alkadiene polymer (Color: Blue)
| Property | Base Material | Standard / Test Method | |
|---|---|---|---|
| ULT Version | LT Version | ||
| Thermal Conductivity | -100°C, 0.028 -165°C, 0.021 |
0°C, 0.033 -50°C, 0.028 |
ASTM C177 |
| Density Range | 60-80 Kg/m³ | 40-60 Kg/m³ | ASTM D1622 |
| Recommend Operation Temperature | -200°C to 125°C | -50°C to 105°C | - |
| Percentage Of Close Areas | > 95% | > 95% | ASTM D2856 |
| Moisture Performance Factor | NA | < 1.96x10⁻¹¹ g/(m.s.Pa) | ASTM E 96 |
| Wet Resistance Factor (μ) | NA | > 10000 | EN12086 / EN13469 |
| Water Vapor Permeability Coefficient | NA | 0.0039 g/h.m² (25mm thickness) | ASTM E 96 |
| PH | ≥ 8.0 | ≥ 8.0 | ASTM C871 |
| Tensile Strength (MPa) | -100°C, 0.30 -165°C, 0.25 |
0°C, 0.15 -50°C, 0.218 |
ASTM D1623 |
| Compressive Strength (MPa) | -100°C, ≤ 0.3 | -40°C, ≤ 0.16 | ASTM D1621 |
The ULT (Ultra-Low Temperature) system is primarily composed of alkadiene polymer and is blue in color. The LT (Low Temperature) system consists of NBR/PVC and is black in color.
The ULT insulation system is recommended for temperatures ranging from -200°C to 125°C, while the LT insulation system is suitable for temperatures from -50°C to 105°C.
No, the insulation system is built with integrated expansion joints, eliminating the need to use fiber materials as expansion and contraction fillers.
The system features a built-in vapor barrier that greatly extends the system's operational lifespan and reduces the risk of corrosion underneath the insulation.
Both the ULT and LT versions feature a closed cell structure area percentage exceeding 95% (tested under ASTM D2856), ensuring excellent moisture and thermal resistance.
According to ASTM D1622 test methods, the density range for the ULT material is 60-80 Kg/m³, and the density range for the LT material is 40-60 Kg/m³.